High ductility brittle crack arrest wear-resistant steel

Home >  Products >  Wear resistant steel plate >  High ductility brittle crack arrest wear-resistant steel

High Ductility Brittle Crack Arrest Wear-Resistant Steel

High Ductility Brittle Crack Arrest Wear-Resistant Steel

Quick Detail:

While ensuring unchanged wear resistance, NM450Tuf products have an impact force of up to 110J at -20°C. The low-temperature toughness is more than 2 times that of wear-resistant steel of the same level, 4 times more than the national standard requirements. It can serve in the -60°C environment and has excellent wear resistance. And the service life is doubled without increasing the cost of welding and other processing techniques.

The main materials are NM400Tuf, NM450Tuf, and NM500Tuf


  • Overview
  • Inquiry
  • Related Products
Place of OriginChina
Brand NameHNJBL
Model NumberNM450Tuf
CertificationBV SGS CE TUV


Minimum Order Quantity1Ton
Packaging DetailsStandard seaworthy export packing or according to the customers' request
Delivery Time7-15 working days after the receipt of 30% deposit
Payment TermsTT or L/C
Supply Ability25000Tons/per month



Description:

High ductility brittle crack arrest wear-resistant steel is a steel developed to solve the problem of cracking in U-shaped dump truck carriages. "Crack-arresting steel" refers to steel with good fracture toughness and the ability to inhibit the propagation of brittle cracks, and has the ability to prevent cracks from expanding at high speeds. . When there are potential defects or cracks in components, the crack arresting steel can prevent the expansion of cracks within a small range and prevent major accidents under the action of dynamic load and impact load.


Specifications:

ModelYield Strength(Rel,MPa)Tensile Strength( Rm,MPa)Elongation(A50,%)Brinell Hardness(HBW)Impact energy(J)
NM400Tuf≥1000≥1200≥10370-430≥48
NM450Tuf≥1100≥1300≥7420-480≥48
NM500Tuf≥1200≥1500≥7≥470≥38



Competitive Advantage:

1.Large Inventory:Provide processing and customization services. We can meet the needs of different steel length and size and large number of procurement.

2.24 Hours Online Service: We will treat every customer with enthusiastic service, every message will reply in minimal time, and actively solve your problem, we will wait for your inquiry 24 hours.

3.We support free samples: you only need to pay shipping to get samples of our products and if you have any questions we will always answer for you and believe our sample service can reassure you to buy our products.

4.Quality assurance:We will guarantee for you that the quality of all the goods is strictly inspected,after passing the products issued for you, and carefully packaged, to ensure that the goods are not damaged during transportation, you can be assured to buy our products.

5.Delivery on time:Our products will be shipped at your required time to reduce your time loss and we will update your shipping progress for you so that you can better time.


Tag:

High Ductility Brittle Crack Arrest Wear-Resistant Steel, ChinaHigh Ductility Brittle Crack Arrest Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,High Ductility Brittle Crack Arrest Wear-Resistant Steel,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel


GET IN TOUCH

Email Address *
Name*
Phone Number*
Company Name*
Message *
Newsletter
Please Leave A Message With Us